epoxy zinc rich primer

epoxy zinc rich primer

人氣:

主要成分:Main ingredients: the paint contains double components. Component A contains epoxy resin, superfine zinc powder, many accessory ingredients and blending solvents. Component B takes Poly carbon amine resin as curing agent.

性  質: acrylic acid series  Vinylidene Chloride series 
用  途: High temperature resistance  terrace 
分  類: Architectural coating 
在線訂購
  • popularity
  • basic information
  • Construction reference

Main ingredients: the paint contains double components. Component A contains epoxy resin, superfine zinc powder, many accessory ingredients and blending solvents. Component B takes Poly carbon amine resin as curing agent.

Properties:

rich zinc primer series

application

anti-corrosive, steel structure, storage tank, chemical equipment, bridge and others

分  類:

工業裝備漆

Classification: industrial equipment paint

ingredients
The paint contains double components. Component A contains epoxy resin, superfine zinc powder, many accessory ingredients and blending solvents. Component B takes Poly carbon amine resin as curing agent.

Properties and application

The paint film has high hardness, strong adhesive force, impact resistance, good corrosion resistance and other features. With strong primer, it doesn’t need to get rid of paint film and takes machining, cutting, welding and other works. So, it is widely used in the surface treatment for all kinds of steel plates, structural steels and others.

technical conditions

test item

technical index

test method

Color and appearance for coating film

Grey and uniform for coating film

GB1729-79

Drying time  hour

GB1728-79

   25℃

Surface drying

1

Actual drying

24

Adhesive force  level

≤2

GB1720-79

3%Nacl

Salty water resistance

no obvious change

GB1763-79

Site matching before using. Brush or spraying coating.
Take surface treatment for the coated material before coating and recommend spraying sand method. De-rusting grade is grade Sa2.5. The steel surface after treatment has no rust, scale free, greasy dirt and impurity. The treated surfaces should be coated in 8 hours.
Mix up component A and B respectively before coating and mix component A and B evenly by ratio 100:9 (weight ratio). After curing 20 minutes, take coating and use up in 4-6hours for mixed paints.
If the paint viscosity is too big, it is not suitable for the construction, and can use the paint diluents to dilute. The diluent amount doesn’t generally exceed 10% of total amounts.
Construction temperature should be above 10℃. The paint is hard for curing below it.
Theoretical amount is about 130g/m2
Every paint thickness is 35*50 micrometer (calculated by dry film)
Coating interval is 12-24 hours

storage and transportation
Valid period is one year. Transportation should follow the relevant regulation from transportation department.
baidu
HOMEAbout usProductsCaseJoinNewsService centerSocial ResponsibilityJOBVideoSite MapLegal NoticesContact us
All rights reserved: Address:No.2, Yulin Avenue, Dadong District, Shenyang, China ICP備案編號:遼ICP備12011664號-1  Phone:024-88208077
亚洲精品国产成人-亚洲国产欧美日韩在线人成-2020亚洲成高清三区二区二区-华人在线亚洲欧美精品